→Ferric Ammonium Oxalate
* 300 ml water
The coating thickness was estimated to be 7 to 9 microns. Plates were three days exposed after coating. Geometry was a two-beam transmission grating at zero degrees and 24 degrees (~900 l/mm) at 457 nm from a solid state Melles Griot laser. The pictured plate was a 60 mJ exposure (mJ/cm^2?).
Processing was as follows: