DCG 45sec exposer 457 nm
film 2.5/12/100
process
1.15 min fix (1/7 fix/water)
1 min water rince
.5 min 35% iso
.5 min 75% iso
1.5 min 91% iso
hot air dry
i also have a 2 color of this that was done 457nm & 532nm that i will post later
Please officer No Ticket
this image does not display what you can see the hologram.
it is a 2 color wideband hologram
1 457nm 45 sec exposer then a 532 15min exposer. you can notice deeper reds and more contrast in the 3 medials copper/gold/silver
same processing as above... i will be trying this again.. maybe more narrow band
it is a 2 color wideband hologram
1 457nm 45 sec exposer then a 532 15min exposer. you can notice deeper reds and more contrast in the 3 medials copper/gold/silver
same processing as above... i will be trying this again.. maybe more narrow band
Please officer No Ticket
Fantastic job Danny, congratulations. I think that's a good idea to try narrowband. If you're doing an object with rather saturated colors (say for example blue and green), it would definitely produce better results going narrowband (assuming you could control the shrinkage of the final DCG layer). But since it's a metallic badge, it's hard to say what would look better, broadband or narrowband (assuming a two-color exposure at 457 and 532) or something in between. I'm looking forward to seeing more of your two-color work. By the way, this is the only kind of stuff you need to do to keep holography going strongDanny Bee wrote:i will be trying this again.. maybe more narrow band
Please officer No Ticket
nice job on the badge hologram! danny what was the AMDI content you used in the two color holo?i see your backround is nice and clear, what was the method you used to clear up these backround areas?
Please officer No Ticket
thanks David ,dave battin wrote:nice job on the badge hologram! danny what was the AMDI content you used in the two color holo?i see your backround is nice and clear, what was the method you used to clear up these backround areas?
2.5 grams AMDI
black velvet
Please officer No Ticket
Outstanding Danny.
It is tough to balance the exposure between very shiny areas and non-shinny one such as lettering.
Hope the customer likes it as much as we do!
It is tough to balance the exposure between very shiny areas and non-shinny one such as lettering.
Hope the customer likes it as much as we do!